Diamond Heat Sink (Thermal Conductivity: 1500W/m.K, Ra < 50nm)
SKU: WA1906
Diamond Heat Sink (Thermal Conductivity: 1500W/m.K, Ra < 50nm)
Polycrystalline diamond (PCD) belongs to wide band gap materials group. It has properties similar to single crystal diamonds (SCD), including exceptional thermal conductivity, high electron mobility, and high power capacity. These properties make it an excellent materials in improving the reliability and enhancing the power density while reducing the size of the power devices. The main differences between PCD and SCD are that PCD has slightly lower thermal conductivity compared with SCD; however, it is more commonly used in industry due to the lower cost and availability in large size. It is used in various applications, including heat spreader, cutting tool, epitaxy substrate, and power electronics. For example, researchers at University of Bath grow epitaxial GaN films on a polycrystalline diamond wafer for high power application resulting in a promising solution for heat dissipation problem.
Specification:
Size |
WA1906: 10mm x 10mm WA1907: 2 inch diameter |
Thickness | 0.3mm |
Thickness Tolerance | ± 5% |
Bulk Resistivity | 1012 ohm.cm |
Surface Resistivity | 1010 ohm.cm |
Thermal Conductivity | 1500W/m.K |
Thermal Diffusivity at 300K | > 8.3cm2s-1 |
Thermal Expansion Coefficient | 1.3 x 10-6K-1 |
Surface#1, Surface Roughness | Ra < 50nm |
Surface#2, Surface Roughness | Ra < 200nm |
Quantity | 1 piece |
*The figure is for reference only. The actual product may look different due to configuration difference.
Please contact us for customization or bulk order.
References: