MSE PRO Flexible Conductive ITO-PET Film Sheet for Solar Cells
SKU: LS2616
MSE PRO™ Flexible Conductive ITO-PET Film Sheet for Solar Cells
MSE Supplies provides Flexible Conductive ITO-PET Film Sheet for Solar Cells. ITO-PET Film is a premium-grade, transparent conductive film crafted with a polyethylene terephthalate (PET) substrate coated with indium tin oxide (ITO). This innovative material combines excellent optical transparency with superior electrical conductivity, making it a preferred choice for a wide range of electronic applications. Lightweight, flexible, and durable, it is ideal for touchscreens, display panels, EMI shielding, and flexible electronics. Its robust chemical and thermal stability ensures reliable performance in demanding environments, while its compatibility with advanced fabrication techniques supports cutting-edge designs in modern technology.
ITO-PET conductive film is suitable for use under test conditions of 80-120°C.
Key Features:
Parameter performance of PET substrate.
| Thickness (mm) | 0.038 | 0.050 | 0.075 | 0.100 | 0.125 | 0.175 | 0.188 | Testing Method (ASTM D374) |
| Tensile Strength MD (MPa) | 184 | 195 | 168 | 162 | 163 | 161 | 161 | (ASTM D882) |
| Tensile Strength TD (MPa) | 202 | 206 | 195 | 174 | 179 | 173 | 183 | (ASTM D882) |
| Elongation at Break MD (%) | 170 | 170 | 160 | 160 | 170 | 180 | 180 | (ASTM D882) |
| Elongation at Break TD (%) | 160 | 170 | 150 | 160 | 170 | 160 | 160 | (ASTM D882) |
| Heat Shrinkage MD (%) | 1.2 | 1.2 | 1.2 | 1.1 | 1.0 | 1.0 | 1.0 | (ASTM D1204) |
| Heat Shrinkage TD (%) | 0.4 | 0.4 | 0.4 | 0.3 | 0.3 | 0.3 | 0.3 | (ASTM D1204) |
| Friction Coefficient Us | 0.41 | 0.39 | 0.37 | 0.39 | 0.39 | 0.39 | 0.37 | (ASTM D1894) |
| Friction Coefficient Ud | 0.38 | 0.35 | 0.33 | 0.36 | 0.36 | 0.35 | 0.35 | (ASTM D1894) |
| Light Transmittance (%) | 90 | 90 | 90 | 90 | 90 | 90 | 90 | (ASTM D1003) |
| Fog (%) | 0.9 | 0.9 | 1.0 | 1.1 | 1.2 | 1.5 | 1.6 | (ASTM D1003) |
Parameter performance of ITO layer.
| Resistance (Ω) | 10 | 15 | 35 | 50 | 100 | Testing Method |
| Thickness (mm) | 0.125/0.17 | 0.125/0.17 | 0.125/0.17 | 0.125/0.17 | 0.075/0.175 | (ASTM D1003) |
| Width (mm) | 800-1220 | 800-1220 | 800-1220 | 800-1220 | 800-1220 | |
| Tensile Strength MD (MPa) | 170-180 | 170-180 | 170-180 | 170-180 | 170-210 | (ASTM D882) |
| Tensile Strength TD (MPa) | 178-186 | 178-186 | 178-186 | 178-186 | 178-220 | (ASTM D882) |
| Elongation at Break MD (%) | 110-135 | 110-135 | 110-135 | 110-135 | 110-150 | (ASTM D882) |
| Elongation at Break TD (%) | 100-110 | 100-110 | 100-110 | 100-110 | 100-130 | (ASTM D882) |
| Heat Shrinkage MD (%) | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 | 130℃ * 30min |
| Heat Shrinkage TD (%) | 0.5 | 0.5 | 0.5 | 0.5 | 0.6 | 130℃ * 30min |
| VLT (%) | >80 | >80 | >80 | >80 | >80 | (ASTM D1003) |
| Fog (%) | <2.5 | <2.5 | <2.5 | <2.5 | <1.5 | (ASTM D1003) |
| ITO Light Transmittance (%) | 85 | 88 | 95 | 98 | 98 | (ASTM D1003) |
| Square Resistance (ohm/sq) | 10 | 15 | 35 | 50 | 100 | Four Probe |
| Uniformity (ohm) | 5 | 5 | 5 | 6 | 20 | (ASTM D991) |
| Coating Adhesion | 100% | 100% | 100% | 100% | 100% | (ASTM D3359) |
| Thermal Test (R/R0) | <1.5 | <1.5 | <1.5 | <1.5 | <1.5 | 110℃ * 30min |
MSE Supplies offers a wide range of laboratory supplies. Please contact us for more information.