MSE PRO LISICON LATP Solid State Electrolyte Membrane, 300um thick, 12mm diameter
SKU: ME0201
MSE PRO LISICON LATP Solid State Electrolyte Membrane, 300um thick, 12mm diameter, lithium aluminum titanium phosphate (LATP)
- SKU# ME0201
- Composition: LATP, Li1.3Al0.3Ti1.7(PO4)3
-
Size (Diameter): 12 mm +/- 0.3 mm
- Thickness: 300 um +/- 10 um
-
Lithium Ionic Conductivity: 2.75 x 10-4 S/cm at room temperature (25C)
- Relative Density: 95%
- Theoretical Density: 2.92 g/cm3
- Membrane Product Density: 2.77 g/cm3
- Flexural Strength: ~140 MPa
- Primary Crystal Structure: NASICON type LATP crystals
-
Applications: The unique properties of Ampcera™ LISICON lithium aluminum titanium phosphate (LATP) membrane solid state electrolyte materials make them ideal choices for all solid state lithium batteries, advanced Lithium-Sulfur, Lithium-Air, Lithium-Water batteries, etc. Ampcera™ LISICON (Lithium-ion Superionic Conductor) LATP membrane materials are used as solid state electrolytes or separators in advanced lithium batteries and other electrochemical devices.
- * All solid state electrolyte materials sold by MSE Supplies are under the trademark of Ampcera.
-
Li-O2 and Li-S batteries with high energy storage Peter G Bruce, Stefan A Freunberger, Laurence J Hardwick, Jean-Marie Tarascon Nat Mater 2012 Jan 15;11(1):19-29.
- Recent advances in all-solid-state rechargeable lithium batteries C Sun, J Liu, Y Gong, DP Wilkinson, J Zhang - Nano Energy, 2017 https://doi.org/10.1016/j.nanoen.2017.01.028
- Elaboration and characterization of a free standing LiSICON membrane for aqueous lithium air battery Laurent Puech, Christophe Cantau, Philippe Vinatier, Gwenaëlle Toussaint, Philippe Stevens
- Membranes in Lithium Ion Batteries Min Yang and Junbo Hou
- Li-ion transport in all-solid-state lithium batteries with LiCoO2 using NASICON-type glass ceramic electrolytes. Power Sources. 2009;189:365370. doi: 10.1016/j.jpowsour.2008.08.015. Xie J., Imanishi N., Zhang T., Hirano A., Takeda Y., Yamamoto O.