MSE PRO LATP solid electrolyte coating separator GMSS01- double-sided single coating L 2+9+2um

MSE PRO LATP solid electrolyte coating separator GMSS01- double-sided single coating L 2+9+2um

SKU: PO8132

  • £4800
  • Save £800



MSE PRO™ LATP solid electrolyte coating separator GMSS01- double-sided single coating L 2+9+2um

Product Details:

Can be used as a control group for routine laboratory testing to study the cathode and anode reactions of LATP. Can be used for liquid lithium batteries, semi-solid lithium batteries, coin cell, and pouch cell, but cannot be used for pure solid state batteries or sodium batteries. Exposed to air is relatively stable, but it is best to operate in a dry room and store it sealed after use.

Roll up and ship in cardboard boxes. Use in a dry environment, dry before use, seal and store after use.

rd boxes. Use in a dry environment, dry before use, seal and store after use.

Specifications

Product model: GMSS01

Product thickness(um)  13.1

Base film thickness PE(um)   8.6

Product width(mm)  97

Breathability(sec/100ml)  201

Surface density(g/m2)  10.5

Puncture Strength Φ1.0mm(gf)  434

Heat shrinkable 130℃×1h MD(%) 1.30

Heat shrinkable 130℃×1h TD(%) 1.35

Tensile strength MD(Kgf/cm2) 1669

Tensile strength TD(Kgf/cm2) 1790

Elongation at breakMD(%) 105

Elongation at breakTD(%) 70

Peel Strength(N/m) 87.3

  • A represents alumina, L represents LATP, and B represents boehmite.

    The thickness of the PE base film is 9um, and the LATP coating of the oxide solid electrolyte on both sides is 2um each, applied on both sides of the PE base film