MSE PRO MP-171 High Performance Anion Exchange Membranes (AEMs)
SKU: ME0505
MSE PRO™ MP-171 High Performance Anion Exchange Membranes (AEMs)
Applications:
This anion exchange membrane (AEM) is a substrate reinforcement membrane with thickness of 10 to 15 µm, high ionic conductivity, very high electrochemical stability in alkaline and oxidation environments, and mechanical stability. It can be widely used in various fields including AEM Electrolyzer, AEM fuel cell, Electrodialysis, Water Treatment and others.
Delivery:
The membrane is the semi-transparent film delivered in the wet or dry form.
Pretreatment:
If the membrane is delivered in the wet chloride form, the following procedure can be used to make the OH- form: (1) soak the membrane in 1M KOH in a closed container at a fixed temperature (25℃~80℃) for over 12 hrs, (2) then rinse with deionized water copious time until pH neutral. The AEM in OH- form should be used in making the cell quickly or be stored in a sealed container in deionized water to avoid exposure to ambient CO2.
Note: Keep membrane package closed/sealed when unused. Store, handle and process the membrane in a clean, dust-free environment.
SKU: ME0505
Pack Size: 1 pc/pack
Image for reference only
Specifications:
| Membrane Type | Anion Exchange Membrane |
| Appearance | Clear, Semi-Transparent |
| Counter Ion | Chloride (Cl-) |
| Thickness (dry) | 10 to 15 um |
| OH- Conductivity at 23.0 °C | 30-36 mS/cm |
| Weight per Unit Area | 1.1-1.3 mg/cm2 |
| Ion Exchange Capacity | 2.2-2.5 meq/g |
| Tensile Strength at 23.0 °C, 50% RH | 80-150 MPa |
| Young's Modulus at 23.0 °C, 50% RH | 1500-2000 MPa |
| Elongation at Break at 23.0 °C, 50% RH | 30-80 % |
| Dimensional Swelling in H2O at 23.0 °C | < 5 % |
| Water Uptake at 23.0 °C | 45-55 % |
| Alkaline Stability in 1 M KOH at 80 °C | >7500 hours |
| Oxidation Stability in Fenton's test at 80 °C | >12 hours |