Specifications for Stainless Steel Vacuum Grinding Jar

• Vacuum grinding jars are designed for milling and grinding operations either in vacuum or under inert gas. Vacuum grinding jars are used primarily with materials that are at risk of oxidization during the grinding process. The strong seal prevents oxygen, water, and other airborne contaminants from interacting with the contents of the jar.
• Grade 304 is the most widely used austenite steel, also known as 18/8 for its composition of 18% chromium and 8% nickel. 304 may be referred to as A2 stainless (not to be confused with A2 grade steel, also named Tool steel, a steel).
• Grinding jars are used in the fields of Metallurgy, Electronics, Construction Material, Ceramics, Chemical Engineering, Light Industry, Medicine, Environmental Protection, Paint, Ink, Geology and so on.
• Each jar set includes grinding jar, jar lid, and silicon vacuum sealing gasket.
• Volume reduction: please note that due to the extra volume of the stainless steel vacuum shell, grinding jars will only fit in planetary mills with a larger holder size. For example, a 50 ml vacuum jar can only fit into a 100 ml size planetary ball mill jar holder.

Note: 316 stainless steel is also available upon request, for more information contact us at sales@msesupplies.com today.

Features of Stainless Steel Vacuum Grinding Jars

Item No.: JV0301

Material: stainless steel (Fe-Cr-Ni)

Grinding Jar Volume: 50 ml (This 50 ml vacuum jar can only fit into a 100 ml size planetary ball mill jar holder.)

Dimensions: Height 57 mm, OD Flange 75.5 mm, OD 49 mm, ID 39 mm, Wall Thickness 10 mm

Compatible with 0.4L planetary ball mill

Max Loading Capacity: 2/3 capacity of the grinding jar

Shape: cylindrical

Density: 8.0 g/cm³

Main Chemical Compositions: Fe (70.6~67.4%), Cr (17~19%), Ni (8~10%)

Hardness: 187 HB

Attachments: lid & silicon sealing gasket

Abrasion Resistance: fairly good

Suitable for: medium-hard, brittle samples

Choice of Grinding Jars & Grinding Balls

In order to prevent excessive abrasion, the hardness of the grinding jars used and of the grinding balls must be higher than that of the material used. Normally, grinding jars and grinding balls of the same material should be chosen.