Thank you!

Your quote has been successfully submitted!

For products requiring additional information, our team will contact you within 1 business day

Failed

There was an error submitting your quote. Please try again.

ZAL-32 Milling Media-Light Density Sintered Zirconia Alumina Beads– MSE Supplies LLC

Free Shipping on MSE PRO Online Orders of $500 or More! U.S. Orders Only * Offer Excludes Hazmat Shipments *

Menu
Cart

This product has been added to the cart.

25 kg Light Density Sintered Zirconia Alumina Composite Beads, ZAL-32 Milling Media - MSE Supplies LLC

25 kg Light Density Sintered Zirconia Alumina Composite Beads, ZAL-32 Milling Media

SKU: BA1161

  • £51500
  • Save £6200

ZAL-32 Milling Media - Light Density Sintered Zirconia Alumina Composite Beads, 25 kg

The ZAL formulation combines the good properties of two advanced ceramic materials (ZrO2 & Al2O3), bringing beads excellent toughness as well as outstanding breakage resistance. Higher density of the media compared with glass could increase the grinding efficiency. And the smooth bead surface offers extremely low wear to the mill internal components. Thus these beads can substitute glass and other low-medium density grinding medias very well.
Please contact us for Bulk Pricing.

Specifications for Light Density Sintered Zirconia Alumina Composite Beads, ZAL-32 Milling Media

Items Specification

Composition
  • Zirconium Oxide (ZrO2): 20 wt.%
  • Silica (SiO2): 35 wt.%
  • Aluminum Oxide (Al2O3): 40 wt.%
  • Remainder: 5 wt.%
SKU#
BA1161: 0.40 - 0.80 mm
BA1162: 0.80 - 1.20 mm
BA1163: 1.20 - 1.50 mm
BA1164: 1.40 - 1.70 mm
BA1165: 1.80 - 2.20 mm
BA1166: 2.00 - 2.50 mm
BA1167: 2.50 - 3.00 mm
BA1168: 3.00 - 4.00 mm
BA1169: 4.00 - 5.00 mm
BA1170: 5.00 - 6.00 mm
Bulk Density 2.2 kg/L
Density 3.15 - 3.30 g/cc
Hardness 854 Hv10
Mohs' Hardness 8
Color White (glossy sheen)
Boiling Point N/A
Melting Point Over 1600 ℃

 

Features of Light Density Sintered Zirconia Alumina Composite Beads, ZAL-32 Milling Media

  1. Light density medias with unique formulations, patented.
  2. Superior price-performance ratio to other low-medium density grinding medias.
  3. Substitute glass beads very well by reducing media & mill wear and increasing grinding efficiency.